120mm Steel Balls for Ball Mill

120mm S teel B alls F or B all M ill Introduction “DongBang” brand 120mm steel balls for ball mill , your best choice for gold ore mine mineral processing, high and even hardness can support you to reduce ball consumption 10-20% based on win-win cooperation. Specifications Application: 120mm...

Inquiry

  • Product Details

120mm Steel Balls For Ball Mill Introduction 
“DongBang” brand 120mm steel balls for ball mill , your best choice for gold ore mine mineral processing, high and even hardness can support you to reduce ball consumption 10-20% based on win-win cooperation.
图片84.png 
Specifications
Application: 120mm Steel Balls For Ball Mill
Grinding Media Ball size: 25mm/30mm/40mm/50mm/60mm/70mm/80mm/90mm/100mm/120mm/125mm
D25MM-100MM Grinding Ball Production Method: Hot Rolling
D100mm-125mm Grinding Ball Production Method: Forging or hot rolling
Steel Rod Supplier: NISCO, HUAI STEEL, ETC

                                                                                  Steel Rod Type: B3, Chemical Comments

C

Si

Mn

P

S

Cr

0.61-0.65

1.73-1.80

0.73-0.80

≤0.020

≤0.015

0.80-0.88

Ni

Cu

Mo

Alt

V


≤0.25

≤0.20





120mm Steel Balls For Ball Mill Quality Performance

Ball Size

Surface Hardness

Core Hardness

Volume Hardness

Impact Toughness

100mm

60-62 HRC

58-60 HRC

58-62 HRC

≥22 J/CM2

120mm

60-62 HRC

58-60 HRC

58-62 HRC

≥24 J/CM2

125mm

60-62 HRC

58-60 HRC

57-61 HRC

≥26 J/CM2

Original: Jiangyin, Jiangsu, China
Certification: ISO9001, ISO14001, OHSAS18001 etc.
Price: Negotiable
Material: Alloy Steel
Payment term: TT, LC

图片85.png

图片86.png

图片87.png

Difference between hot rolled grinding balls and casted balls: 

1. Difference in density

As hot rolled grinding balls are based on round steel rod, which is produced by hot rolled extrusion of square billets. During the production of hot rolled balls, they are formed and extruded by rollers, so the density of hot rolled grinding balls is usually more than 7.89. 

The casted balls, due to use of traditional casting process, it is hard to avoid pores and sand inclusions inside the casted balls and on the surface of them or casting trimming etc., so the density is usually around 7.45. 

2. Difference is quality uniformity

As hot rolled grinding balls adopt finished round steel and have unified quality, the round steel will pass through natural gas heating furnace(or induction furnace), rolling machine, quenching system, tempering furnace, cooling plate and packing machine etc., in which a mechanized flow line operating mode has been achieved in the whole production process. The temperature, speed and technical parameters are controlled by computer tracking and ensure the production to be stable and uniform. 

The steel scraps used for casted balls are likely to be uneven in material itself. Besides, the batching proportion of each furnace and casting speed are liable to influence of human factors and the quality of products is hard to keep stable. 

3. Difference in impact toughness and crus resistance

Due to high density and impact toughness≥18(J/CM2) of hot rolled grinding balls, the fatigue life of 6m height falling ball impact test is ≥ 20,000 times, so the breaking rate is quite lower. 

Generally, the impact toughness of casted balls is ≤4(J/CM2) due to pores and sand inclusions, it cannot be performed with falling ball impact test, so it has a higher breaking rate risk. 